Heterogeneous ZieglerNatta catalysts with various sizes of MgCl2 crystallites : synthesis and characterization
AuthorRedzic, Eldin ; Garoff, Thomas ; Mardare, Cezarina Cela ; List, Manuela ; Hesser, Günter ; Mayrhofer, Leonhard ; Hassel, Achim Walter ; Paulik, Christian
Published in
Iranian Polymer Journal, 2016, Vol. 25, Issue 4, page 321-337
PublishedSpringer, 2016
LanguageEnglish
Document typeJournal Article
Keywords (EN)ZieglerNatta catalyst / Crystallite size / Synthesis / Characterization / Polyethylene
ISSN1735-5265
URNurn:nbn:at:at-ubl:3-1383 Persistent Identifier (URN)
DOI10.1007/s13726-016-0424-x 
Restriction-Information
 The work is publicly available
Files
Heterogeneous ZieglerNatta catalysts with various sizes of MgCl2 crystallites [1.97 mb]
Links
Reference
Classification
Abstract (English)

A MgCl2-based ZieglerNatta catalyst was characterized using X-ray diffraction (XRD) patterns, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) and IR spectra. We focused on the XRD reflection at 2 = 50 to determine the thickness of MgCl2 crystals, and validated these results with TEM pictures. SEM pictures were taken in order to measure the size of the nanoparticles formed by the MgCl2 crystals. Several compounds were synthesized for comparison and to aid interpretation of the infrared (IR) spectra. The catalysts were prepared by precipitating MgCl2, which was used as support material and subsequently treated with TiCl4. The thickness of the catalyst crystals was calculated from the XRD reflection at 2 = 50. Changing the precipitation temperature within a range from 40 to 90 C altered the thickness of the MgCl2 crystal plates. The maximum thickness of 7 nm was achieved at a precipitation temperature of 60 C. The SEM pictures showed that the nanoparticles had a diameter of 200 nm. A crystal base unit had a volume that corresponded to that of a sphere of 3.5 nm radius. Thus, we estimated that a typical catalyst particle with a diameter of 20 m contained about one million nanoparticles, each of which consisted of about 25,000 MgCl2 crystal units.